Neoprene GW polychloroprene rubber Dupont Dow Elastomers Rubber - Elastomer >> Chlorinated rubber / Chloroprene, CR ADHESIVE Adhesives Neoprene GW is a sulfur-modified polychloroprene stabilized with a thiuram disulfide. The crystallization rate of Neoprene GW is slightly faster than that of Neoprene GRT. Compounds of Neoprene GW cured with metal oxides alone have excellent processing safety, yet cure rapidly. Although not required, cure accelerators can be used and are advantageous for some applications. Properly compounded vulcanizates of Neoprene GW have high resilience and excellent flex cracking resistance, and the best tear strength of any type of Neoprene. Vulcanizates of Neoprene GW retain their properties after heat-aging better than other G types. Compression set resistance is significantly improved over that of other G types, although it is not as good as that of thiourea-cured W types. Neoprene GW breaks down, or softens, to a lesser degree than other G types. Compounds based on Neoprene GW will therefore exhibit a higher viscosity than similarly loaded compounds based on Neoprene GNA or GRT. Because of the higher compound viscosity, stocks based on Neoprene GW are slightly less sticky and have slightly less building tack than stocks based on other G types. Compounds of Neoprene GW have approximately the same viscosity as do similarly loaded compounds of Neoprene W. Sulfur-modified polychloroprene stabilized with a thiuram disulfide. Provides good processing safety and rapid cure in compounds cured with metal oxides. Offers high resilience, good flex cracking resistance, and good tear strength in compounded vulcanizates.